Various Colors FKM Rubber Compound with Low Compression Set and Fuel Resistance for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Ms. Ada

yguo@dowhon.com

8613753601944

Contact Now

Various Colors FKM Rubber Compound with Low Compression Set and Fuel Resistance for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore A:

65-90

Compression Set:

Thickness:

2mm-8mm

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness Shore A:

75±5

Elongation At Break:

Min200

Tensile Strength:

Min11.0 MPa

Compression Set 200°C:

Max15%

Brittleness Temperature:

-26°C

Hardness Change:

2 Degree

Tensile Change:

-2%

Volume Change ASTM 1#:

0.4%

Volume Change ASTM 3#:

2.1%

Net Weight:

25kg

Highlight:

Various Colors FKM Rubber Compound

Low Compression Set Fluoroelastomer Compound

Fuel Resistance Fluoroelastomer Rubber

Product Description

Company Profile

Founded in 2002, headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

The largest FKM manufacturer in China, with actual output of 5500mt in 2022
2 CNAS approved laboratories
1 10,000 classification workshop for smart-wearable devices
1 100,000 classification workshop for FKM precompounds and compounds
23 production lines for FKM precompounds and compounds

Product Description

Fluoroelastomer DHF-75611F

Typical Properties

Property	Value
F Content	Min 66%
Specific Gravity	Min 1.92
Physical Form	Slab
Color	Various
Solubility	Ketones and Esters
Hardness (Shore A)	75±5

Instruction

DHF-75611F is a fluoroelastomer compound containing copolymer of hexafluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gaskets and O-rings, DHF-75611F is a compound ready for direct final product manufacturing.

Features

Excellent mold release
Excellent hot tear resistance
Good mold flow
Low compression set

Packing Information

DHF-75611F is packaged with PE film in cartons. Net weight is 25kg per carton.

Safety and Handling

Store in well ventilated place
Smoking strictly forbidden in working areas
Avoid eye contact
Wash thoroughly any contacted skin and clothing after handling

Typical Physical Properties

Press Cure 180ºC@5min, Post Cure 230ºC@24hour

Property	Value	Test Method
Hardness, Shore A	75±5	ASTM D 412
Elongation at Break, %	Min 200	ASTM D 412
Tensile, MPa	Min 11.0	ASTM D 2240
Compression Set % 200ºC@70hour	Max 15	ASTM D 395 method B Disc

Low Temperature Resistance

Brittleness temperature: -26ºC (ASTM D 1329)

Air Oven Aging ASTM D-537, 230ºC@70h

Property	Change
Hardness change, degree	2
Tensile change %	-2
Elongation at break change %	0

Oil Resistance ASTM D471 Standard, 150ºC@70h

ASTM 1# Standard Oil

Property	Change
Hardness change, degree	2
Tensile change %	0
Elongation at break change %	0
Volume Change %	0.4

ASTM 3# Standard Oil

Property	Change
Hardness change, degree	6
Tensile change %	-4
Elongation at break change %	2
Volume Change %	2.1

Detailed Photos

Packaging & Shipping

20kg/25kg per carton by courier (FedEx, DHL, etc.); 500kg/625kg/700kg per pallet for shipping.

Installation Instructions

Certifications

ISO9001, ISO14001, ISO16949

Currently holds 109 patents, with 21 invention patents under application, participated in formulation of 4 National Standards.

Gazelle Enterprise of Sichuan Province
Technologically Advanced Little Giant Enterprise
National High-Tech Enterprise
Key Cultivation New Material Enterprise of Sichuan Province
Key New Material Enterprise of Chengdu
Transform and upgrading advanced enterprises
Enterprise Technology Center of Sichuan Province
Member Unit of China Fluorinated and Silicone Association Council

Frequently Asked Questions

What's your MOQ?
By air MOQ is 20-25kg, by sea MOQ is 100kg.
What's your delivery time?
For stock goods: delivery within 3 working days. Otherwise: 7-14 working days.
What's your package?
Usually packaged with PE film in cartons (20-25kg net per carton). 500kg/625kg/700kg per pallet.
How can we select the exact grade for our usage?
Please contact our sales team for recommendations based on your specific physical properties and requirements.

Tags:

FKM Rubber Compound

FKM Compounds

Eco FKM Rubber Compound

Products Details

Home > Products >

FKM Rubber Compound

Various Colors FKM Rubber Compound with Low Compression Set and Fuel Resistance for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Various Colors FKM Rubber Compound with Low Compression Set and Fuel Resistance for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore A:

65-90

Compression Set:

Thickness:

2mm-8mm

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness Shore A:

75±5

Elongation At Break:

Min200

Tensile Strength:

Min11.0 MPa

Compression Set 200°C:

Max15%

Brittleness Temperature:

-26°C

Hardness Change:

2 Degree

Tensile Change:

-2%

Volume Change ASTM 1#:

0.4%

Volume Change ASTM 3#:

2.1%

Net Weight:

25kg

Minimum Order Quantity:

Price:

8.5

Highlight:

Various Colors FKM Rubber Compound

Low Compression Set Fluoroelastomer Compound

Fuel Resistance Fluoroelastomer Rubber

Product Description

Company Profile

Founded in 2002, headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

The largest FKM manufacturer in China, with actual output of 5500mt in 2022
2 CNAS approved laboratories
1 10,000 classification workshop for smart-wearable devices
1 100,000 classification workshop for FKM precompounds and compounds
23 production lines for FKM precompounds and compounds

Product Description

Fluoroelastomer DHF-75611F

Typical Properties

Property	Value
F Content	Min 66%
Specific Gravity	Min 1.92
Physical Form	Slab
Color	Various
Solubility	Ketones and Esters
Hardness (Shore A)	75±5

Instruction

DHF-75611F is a fluoroelastomer compound containing copolymer of hexafluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gaskets and O-rings, DHF-75611F is a compound ready for direct final product manufacturing.

Features

Excellent mold release
Excellent hot tear resistance
Good mold flow
Low compression set

Packing Information

DHF-75611F is packaged with PE film in cartons. Net weight is 25kg per carton.

Safety and Handling

Store in well ventilated place
Smoking strictly forbidden in working areas
Avoid eye contact
Wash thoroughly any contacted skin and clothing after handling

Typical Physical Properties

Press Cure 180ºC@5min, Post Cure 230ºC@24hour

Property	Value	Test Method
Hardness, Shore A	75±5	ASTM D 412
Elongation at Break, %	Min 200	ASTM D 412
Tensile, MPa	Min 11.0	ASTM D 2240
Compression Set % 200ºC@70hour	Max 15	ASTM D 395 method B Disc

Low Temperature Resistance

Brittleness temperature: -26ºC (ASTM D 1329)

Air Oven Aging ASTM D-537, 230ºC@70h

Property	Change
Hardness change, degree	2
Tensile change %	-2
Elongation at break change %	0

Oil Resistance ASTM D471 Standard, 150ºC@70h

ASTM 1# Standard Oil

Property	Change
Hardness change, degree	2
Tensile change %	0
Elongation at break change %	0
Volume Change %	0.4

ASTM 3# Standard Oil

Property	Change
Hardness change, degree	6
Tensile change %	-4
Elongation at break change %	2
Volume Change %	2.1

Detailed Photos

Packaging & Shipping

20kg/25kg per carton by courier (FedEx, DHL, etc.); 500kg/625kg/700kg per pallet for shipping.

Installation Instructions

Certifications

ISO9001, ISO14001, ISO16949

Currently holds 109 patents, with 21 invention patents under application, participated in formulation of 4 National Standards.

Gazelle Enterprise of Sichuan Province
Technologically Advanced Little Giant Enterprise
National High-Tech Enterprise
Key Cultivation New Material Enterprise of Sichuan Province
Key New Material Enterprise of Chengdu
Transform and upgrading advanced enterprises
Enterprise Technology Center of Sichuan Province
Member Unit of China Fluorinated and Silicone Association Council

Frequently Asked Questions

What's your MOQ?
By air MOQ is 20-25kg, by sea MOQ is 100kg.
What's your delivery time?
For stock goods: delivery within 3 working days. Otherwise: 7-14 working days.
What's your package?
Usually packaged with PE film in cartons (20-25kg net per carton). 500kg/625kg/700kg per pallet.
How can we select the exact grade for our usage?
Please contact our sales team for recommendations based on your specific physical properties and requirements.

Tags: