Dowhon FKM Rubber Compound Low Compression Set High Temperature Resistance Fluoroelastomer for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Ms. Ada

yguo@dowhon.com

8613753601944

Contact Now

Dowhon FKM Rubber Compound Low Compression Set High Temperature Resistance Fluoroelastomer for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore Hardness:

65-90

Compression Set:

Thickness:

2mm-8mm

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness (Shore A):

75±5

Elongation At Break:

Min200%

Tensile Strength:

Min11.0 MPa

Brittleness Temperature:

-26ºC

Press Cure:

180ºC@5min

Post Cure:

230ºC@24hour

Oil Resistance:

150ºC@70h

Volume Change (1# Oil):

0.4%

Volume Change (3# Oil):

2.1%

Package Weight:

25kg Per Carton

Highlight:

Low Compression Set FKM Rubber Compound

High Temperature Resistance Fluoroelastomer Compound

Automotive Industry Application Fluorocarbon Rubber

Product Description

Company Overview

Founded in 2002 and headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

Largest FKM manufacturer in China with annual production of 5500mt in 2022
2 CNAS approved laboratories
10,000 classification workshop for smart-wearable devices
100,000 classification workshop for FKM precompounds and compounds
21 production lines for FKM precompounds and compounds

Product Specifications: DHF-75611F Fluoroelastomer

Typical Properties

Property	Value
F Content	Min 66%
Specific Gravity	Min 1.92
Physical Form	Slab
Color	Various
Solubility	Ketones and Esters
Hardness (Shore A)	75±5

Product Description

DHF-75611F is a fluoroelastomer compound containing copolymer of hexa-fluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gaskets and O-rings, DHF-75611F is a ready-to-use compound for direct final product manufacturing.

Key Features

Excellent mold release properties
Superior hot tear resistance
Good mold flow characteristics
Low compression set

Packaging Information

DHF-75611F is packaged with PE film in cartons. Net weight: 25kg per carton.

Safety and Handling

Store in well-ventilated areas
Strictly no smoking in working areas
Avoid eye contact
Wash thoroughly after handling any contacted skin and clothing

Detailed Physical Properties

Press Cure: 180ºC @ 5min, Post Cure: 230ºC @ 24hour

Property	Value	Test Method
Hardness, Shore A	75±5	ASTM D 412
Elongation at Break, %	Min 200	ASTM D 412
Tensile, MPa	Min 11.0	ASTM D 2240
Compression Set % 200ºC@70hour	Max 15	ASTM D 395 method B Disc

Low Temperature Resistance

Brittleness Temperature, ºC

-26

ASTM D 1329

Air Oven Aging (ASTM D-537, 230ºC@70h)

Property	Change
Hardness Change	+2 degrees
Tensile Change %	-2%
Elongation at Break Change %	0%

Oil Resistance (ASTM D471, 150ºC@70h)

ASTM 1# Standard Oil

Property	Change
Hardness Change	+2 degrees
Tensile Change %	0%
Elongation at Break Change %	0%
Volume Change %	+0.4%

ASTM 3# Standard Oil

Property	Change
Hardness Change	+6 degrees
Tensile Change %	-4%
Elongation at Break Change %	+2%
Volume Change %	+2.1%

Product Images

Packaging & Shipping

20kg/25kg per carton via courier (FedEx, DHL, etc.); 500kg/625kg/700kg per pallet for shipping.

Installation Instructions

Certifications & Accolades

ISO9001, ISO14001, ISO16949

Currently holds 65 patents, with 15 invention patents under application. Participated in formulation of 4 National Standards.

Gazelle Enterprise of Sichuan Province
Technologically Advanced Little Giant Enterprise
National High-Tech Enterprise
Key Cultivation New Material Enterprise of Sichuan Province
Key New Material Enterprise of Chengdu
Transform and Upgrading Advanced Enterprises
Enterprise Technology Center of Sichuan Province
Member Unit of China Fluorinated and Silicone Association Council

Frequently Asked Questions

What is your minimum order quantity (MOQ)?

By air: 20-25kg; By sea: 100kg.

What is your delivery time?

For stock goods: delivery within 3 working days; Otherwise: 7-14 working days.

What is your packaging?

Typically packaged with PE film in cartons (20-25kg net per carton). 500kg/625kg/700kg per pallet.

How can we select the appropriate grade for our application?

Please contact our sales team. We will recommend suitable grades based on your specific physical property requirements and application information.

Tags:

FKM Rubber Compound

FKM Compounds

Eco FKM Rubber Compound

Products Details

Home > Products >

FKM Rubber Compound

Dowhon FKM Rubber Compound Low Compression Set High Temperature Resistance Fluoroelastomer for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Dowhon FKM Rubber Compound Low Compression Set High Temperature Resistance Fluoroelastomer for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore Hardness:

65-90

Compression Set:

Thickness:

2mm-8mm

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness (Shore A):

75±5

Elongation At Break:

Min200%

Tensile Strength:

Min11.0 MPa

Brittleness Temperature:

-26ºC

Press Cure:

180ºC@5min

Post Cure:

230ºC@24hour

Oil Resistance:

150ºC@70h

Volume Change (1# Oil):

0.4%

Volume Change (3# Oil):

2.1%

Package Weight:

25kg Per Carton

Minimum Order Quantity:

Price:

8.5

Highlight:

Low Compression Set FKM Rubber Compound

High Temperature Resistance Fluoroelastomer Compound

Automotive Industry Application Fluorocarbon Rubber

Product Description

Company Overview

Founded in 2002 and headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

Largest FKM manufacturer in China with annual production of 5500mt in 2022
2 CNAS approved laboratories
10,000 classification workshop for smart-wearable devices
100,000 classification workshop for FKM precompounds and compounds
21 production lines for FKM precompounds and compounds

Product Specifications: DHF-75611F Fluoroelastomer

Typical Properties

Property	Value
F Content	Min 66%
Specific Gravity	Min 1.92
Physical Form	Slab
Color	Various
Solubility	Ketones and Esters
Hardness (Shore A)	75±5

Product Description

DHF-75611F is a fluoroelastomer compound containing copolymer of hexa-fluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gaskets and O-rings, DHF-75611F is a ready-to-use compound for direct final product manufacturing.

Key Features

Excellent mold release properties
Superior hot tear resistance
Good mold flow characteristics
Low compression set

Packaging Information

DHF-75611F is packaged with PE film in cartons. Net weight: 25kg per carton.

Safety and Handling

Store in well-ventilated areas
Strictly no smoking in working areas
Avoid eye contact
Wash thoroughly after handling any contacted skin and clothing

Detailed Physical Properties

Press Cure: 180ºC @ 5min, Post Cure: 230ºC @ 24hour

Property	Value	Test Method
Hardness, Shore A	75±5	ASTM D 412
Elongation at Break, %	Min 200	ASTM D 412
Tensile, MPa	Min 11.0	ASTM D 2240
Compression Set % 200ºC@70hour	Max 15	ASTM D 395 method B Disc

Low Temperature Resistance

Brittleness Temperature, ºC

-26

ASTM D 1329

Air Oven Aging (ASTM D-537, 230ºC@70h)

Property	Change
Hardness Change	+2 degrees
Tensile Change %	-2%
Elongation at Break Change %	0%

Oil Resistance (ASTM D471, 150ºC@70h)

ASTM 1# Standard Oil

Property	Change
Hardness Change	+2 degrees
Tensile Change %	0%
Elongation at Break Change %	0%
Volume Change %	+0.4%

ASTM 3# Standard Oil

Property	Change
Hardness Change	+6 degrees
Tensile Change %	-4%
Elongation at Break Change %	+2%
Volume Change %	+2.1%

Product Images

Packaging & Shipping

20kg/25kg per carton via courier (FedEx, DHL, etc.); 500kg/625kg/700kg per pallet for shipping.

Installation Instructions

Certifications & Accolades

ISO9001, ISO14001, ISO16949

Currently holds 65 patents, with 15 invention patents under application. Participated in formulation of 4 National Standards.

Gazelle Enterprise of Sichuan Province
Technologically Advanced Little Giant Enterprise
National High-Tech Enterprise
Key Cultivation New Material Enterprise of Sichuan Province
Key New Material Enterprise of Chengdu
Transform and Upgrading Advanced Enterprises
Enterprise Technology Center of Sichuan Province
Member Unit of China Fluorinated and Silicone Association Council

Frequently Asked Questions

What is your minimum order quantity (MOQ)?

By air: 20-25kg; By sea: 100kg.

What is your delivery time?

For stock goods: delivery within 3 working days; Otherwise: 7-14 working days.

What is your packaging?

Typically packaged with PE film in cartons (20-25kg net per carton). 500kg/625kg/700kg per pallet.

How can we select the appropriate grade for our application?

Please contact our sales team. We will recommend suitable grades based on your specific physical property requirements and application information.

Tags: