FKM Rubber Compound

Terpolymer Fluoroelastomer Rubber Compound FKM Low Compression Set for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Ms. Ada

yguo@dowhon.com

8613753601944

Contact Now

Terpolymer Fluoroelastomer Rubber Compound FKM Low Compression Set for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore A:

65-90

Compression Set:

Thickness:

2mm-8mm

Width:

As Require

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness Shore A:

75±5

Elongation At Break:

Min200

Tensile Strength:

Min11.0 MPa

Compression Set Max:

15%

Brittleness Temperature:

-26ºC

Hardness Change:

2 Degree

Tensile Change:

-2%

Volume Change:

0.4%

Package Weight:

25kg

Highlight:

Low Compression Set FKM Rubber Compound

Automotive Industry Fluoroelastomer Rubber

Terpolymer FKM Compound

Product Description

Company Profile

Founded in 2002, headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

The largest FKM manufacturer in China, with actual output of 5500mt in 2022
2 CNAS approved labs
1 10,000 clarification workshop for smart-wearable devices
1 100,000 clarification workshop for FKM precompounds and compounds
21 producing lines for FKM precompounds and compounds

Product Description

Fluoroelastomer DHF-75611F

Typical Properties

F Content	Min 66%
Specific Gravity	Min 1.92
Physical form	Slab
Color	VARIOUS
Solubility	Ketones and Esters
Hardness (shore A)	75±5

Instruction

DHF-75611F is a fluoroelastomer compound which includes copolymer of hexa-fluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gasket and O-ring applications, DHF-75611F is a compound ready for direct final product manufacturing.

Features

Excellent mold release
Excellent hot tear resistance
Good mold flow
Low compression set

Packing Information

DHF-75611F is packaged with PE film in cartons. The weight is 25kg net per carton.

Safety and Handling

Store in well ventilated place
Smoking is strictly forbidden in working areas
Avoid eye contact
Wash thoroughly any contacted skin and clothing after handling

Typical Physical Properties

Press Cure 180ºC@5min, Post Cure 230ºC@24hour

Hardness, Shore A	75±5 (ASTM D 412)
Elongation at Break, %	Min 200 (ASTM D 412)
Tensile, MPa	Min 11.0 (ASTM D 2240)
Compression set % 200ºC@70hour	Max 15 (ASTM D 395 method B Disc)

Low Temperature Resistance

Brittleness temperature, ºC

-26 (ASTM D 1329)

Air Oven Aging ASTM D-537, 230ºC@70h

Hardness change, degree	2
Tensile change %	-2
Elongation at break change %	0

Oil Resistance ASTM D471 Standard, 150ºC@70h

ASTM 1# Standard Oil

Hardness change, degree	2
Tensile change %	0
Elongation at break change %	0
Volume Change %	0.4

ASTM 3# Standard Oil

Hardness change, degree	6
Tensile change %	-4
Elongation at break change %	2
Volume Change %	2.1

Detailed Photos

Packaging & Shipping

20kgs/25kgs per carton by courier (FedEx, DHL, etc.); 500kgs/625kgs/700kgs per pallet for shipping.

Installation Instructions

Certifications

ISO9001, ISO14001, ISO16949

Currently holds 65 patents, with 15 invention patents under application, and participated in the formulation of 4 National Standards.

"Gazelle Enterprise of Sichuan Province"
"Technologically Advanced Little Giant Enterprise"
"National High-Tech Enterprise"
"Key Cultivation New Material Enterprise of Sichuan Province"
"Key New Material Enterprise of Chengdu"
"Transform and upgrading advanced enterprises"
"Enterprise Technology Center of Sichuan Province"
"Member Unit of China Fluorinated and Silicone Association Council"

Frequently Asked Questions

What's your MOQ?
BY air MOQ is 20-25KG, by sea MOQ is 100KG.
What's your delivery time?
For stock goods, delivery within 3 working days; otherwise 7-14 working days.
What's your package?
Usually packaged with PE film in carton (20-25kg net per carton). 500kgs/625kgs/700kgs per pallet.
How can we select the exactly grade which suit for our usage?
Please contact our sales team for recommendations based on your specific physical properties and application requirements.

Tags:

FKM Rubber Compound

FKM Compounds

Eco FKM Rubber Compound

Products Details

Home > Products >

FKM Rubber Compound

Terpolymer Fluoroelastomer Rubber Compound FKM Low Compression Set for Automotive Industry

All Category

FKM Rubber Precompound

FKM Rubber Compound

FKM Low Temperature

FKM Fluorine Rubber

Fluoroelastomer Rubber

HNBR Compound

FVMQ Rubber Compounds

FFKM O Rings

VMQ Compound

FFKM Compound

Rubber Additives

Fluorosilicone Rubber

Fluorocarbon Rubber

Terpolymer Fluoroelastomer Rubber Compound FKM Low Compression Set for Automotive Industry

MOQ:	20
Price:	8.5

Detail Information

Product Description

Detail Information

Shore A:

65-90

Compression Set:

Thickness:

2mm-8mm

Width:

As Require

Fluorine Content:

Min 66%

Specific Gravity:

Min1.92

Hardness Shore A:

75±5

Elongation At Break:

Min200

Tensile Strength:

Min11.0 MPa

Compression Set Max:

15%

Brittleness Temperature:

-26ºC

Hardness Change:

2 Degree

Tensile Change:

-2%

Volume Change:

0.4%

Package Weight:

25kg

Minimum Order Quantity:

Price:

8.5

Highlight:

Low Compression Set FKM Rubber Compound

Automotive Industry Fluoroelastomer Rubber

Terpolymer FKM Compound

Product Description

Company Profile

Founded in 2002, headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.

The largest FKM manufacturer in China, with actual output of 5500mt in 2022
2 CNAS approved labs
1 10,000 clarification workshop for smart-wearable devices
1 100,000 clarification workshop for FKM precompounds and compounds
21 producing lines for FKM precompounds and compounds

Product Description

Fluoroelastomer DHF-75611F

Typical Properties

F Content	Min 66%
Specific Gravity	Min 1.92
Physical form	Slab
Color	VARIOUS
Solubility	Ketones and Esters
Hardness (shore A)	75±5

Instruction

DHF-75611F is a fluoroelastomer compound which includes copolymer of hexa-fluoropropylene and vinylidene-fluoride, curatives and fillers.

Applications

Designed for gasket and O-ring applications, DHF-75611F is a compound ready for direct final product manufacturing.

Features

Excellent mold release
Excellent hot tear resistance
Good mold flow
Low compression set

Packing Information

DHF-75611F is packaged with PE film in cartons. The weight is 25kg net per carton.

Safety and Handling

Store in well ventilated place
Smoking is strictly forbidden in working areas
Avoid eye contact
Wash thoroughly any contacted skin and clothing after handling

Typical Physical Properties

Press Cure 180ºC@5min, Post Cure 230ºC@24hour

Hardness, Shore A	75±5 (ASTM D 412)
Elongation at Break, %	Min 200 (ASTM D 412)
Tensile, MPa	Min 11.0 (ASTM D 2240)
Compression set % 200ºC@70hour	Max 15 (ASTM D 395 method B Disc)

Low Temperature Resistance

Brittleness temperature, ºC

-26 (ASTM D 1329)

Air Oven Aging ASTM D-537, 230ºC@70h

Hardness change, degree	2
Tensile change %	-2
Elongation at break change %	0

Oil Resistance ASTM D471 Standard, 150ºC@70h

ASTM 1# Standard Oil

Hardness change, degree	2
Tensile change %	0
Elongation at break change %	0
Volume Change %	0.4

ASTM 3# Standard Oil

Hardness change, degree	6
Tensile change %	-4
Elongation at break change %	2
Volume Change %	2.1

Detailed Photos

Packaging & Shipping

20kgs/25kgs per carton by courier (FedEx, DHL, etc.); 500kgs/625kgs/700kgs per pallet for shipping.

Installation Instructions

Certifications

ISO9001, ISO14001, ISO16949

Currently holds 65 patents, with 15 invention patents under application, and participated in the formulation of 4 National Standards.

"Gazelle Enterprise of Sichuan Province"
"Technologically Advanced Little Giant Enterprise"
"National High-Tech Enterprise"
"Key Cultivation New Material Enterprise of Sichuan Province"
"Key New Material Enterprise of Chengdu"
"Transform and upgrading advanced enterprises"
"Enterprise Technology Center of Sichuan Province"
"Member Unit of China Fluorinated and Silicone Association Council"

Frequently Asked Questions

What's your MOQ?
BY air MOQ is 20-25KG, by sea MOQ is 100KG.
What's your delivery time?
For stock goods, delivery within 3 working days; otherwise 7-14 working days.
What's your package?
Usually packaged with PE film in carton (20-25kg net per carton). 500kgs/625kgs/700kgs per pallet.
How can we select the exactly grade which suit for our usage?
Please contact our sales team for recommendations based on your specific physical properties and application requirements.

Tags: